Introduction to Light weight silica insulation brick

 

Light weight silica insulation brick is also called Light Weight Silica fire Brick. Lightweight refractory material with silicon dioxide above 91% and bulk density below 1.2g/cm3. The refractoriness and softening temperature under load are not much different from ordinary silica bricks with the same composition. However, due to the many pores, the compressive strength, slag resistance, and corrosion resistance are not as good as ordinary silica bricks, but the thermal shock resistance has been improved.

 

 

 

Raw material of Light Weight Silica fire Brick

 

Lightweight silica bricks use finely divided silica as raw materials, and their critical particle size is usually not more than 1mm, and the particles smaller than 0.5mm are not less than 90%. It is prepared by adding flammable substances to the ingredients or adopting the gas generation method to form a porous structure and firing. Can also be made into unburnt products. It is mainly used for all parts of the kiln that requires heat insulation or lightening of its own weight without direct contact with the melt, free from corrosive gas, and not subject to sudden temperature changes. It is used at high temperature and cannot be in contact with alkaline refractory materials. According to different materials, the highest operating temperature is 1200~1550℃.

 

 

 

The mineral composition of Light Weight Silica fire Brick

 

Phosphorite is 78% to 86%, cristobalite is 13% to 15%, and quartz is 4% to 7%. The bulk density is 0.9 to 1.19 g/cm3, the compressive strength is 2.0 to 5.9 MPa, and the thermal conductivity is 0.35 to 0.42 W·(m·K). It has excellent fire resistance. Its softening temperature under load is close to 1620℃ for dense silica bricks, with only a small residual expansion, and its thermal stability is better than dense silica bricks.

 

 

Product Applications

Application of Light Weight Silica fire Brick

 

Generally Light Weight Silica fire Brick can be divided into two levels: the first grade can be used in the top of the steel rolling furnace and the silicate industrial kiln roof, and can be directly in contact with the flame; the second grade is used in the general industrial kiln Insulation. Applicable to: industrial furnaces such as coke ovens, hot blast furnaces, glass melting furnaces and carbon calciners. It has excellent fire resistance. Its softening temperature under load is close to 1620℃ for dense silica bricks, with only a small residual expansion, and its thermal stability is better than dense silica bricks. Therefore, siliceous heat insulating refractory bricks can be used for a long time under high temperature conditions (1500-1550°C) without contact with molten slag, but they are especially suitable for high temperature hot blast furnaces of large blast furnaces. Thermal insulation of silica brick gas.

 

 

Technical conditions for Light Weight Silica fire Brick used in glass kilns

 

Lightweight silicon insulation brick is a kind of heat insulation refractory with the content of SiO2 not less than 91%, which is mainly made of silica.Lightweight silica insulating brick volume density of 0.9 ~ 1.1 g/cm3, thermal conductivity is only half of ordinary silica brick, good thermal shock resistance, the rul start temperature can reach 1600 ℃, far above the clayey insulating brick.Thus the siliceous insulating brick highest use temperature is 1550 ℃.It doesn't contract at high temperatures and even dips slightly. 

 

Refractory fire light weight Light Weight Silica fire Brick  are usually made from crystalline quartzite and contain inflammable materials, such as coke and anthracite sawdust, or form porous structures by gas foaming.Similar to the production industry of ordinary silica bricks, some mineralized agents (CaO, Fe2O3) were added into the ingredients to promote the transformation of quartz, and the strength of the bricks was obtained by using the waste pulp as the binder.When coke or anthracite is used as fuel, because ash is carried into Fe2O3 and Al2O3, no additional iron phosphorus is added to the mix.Lightweight silica brick firing, should maintain strong oxidizing flame before 1200 ℃, make join completely burn out. 

 

 Packaging of Light Weight Silica fire Brick

 

1.on wooden pallets with plastic cover: wooden pallet size :930*930 or 1000*1000mm,

2.Load weight of each pallet: 1.5-2.0 tons,

3.230*114*65mm:512PCS/Pallet, 230*114*75mm:448PCS/Pallet.

 

 

 Shipping of Light Weight Silica fire Brick

1.Our packaging is as per customer’s request

2.Normal goods delivered by sea transport

3.Sample shipping by express

4.We will shipping and delivery goods timely, quanlity and quantity guaranteed, and also in accordance with the contract and customer's requirment completely.