High alumina refractory ball
2021-12-29
High-aluminum refractory balls are also called high-aluminum heat storage balls. High-aluminum refractory balls are made of high-alumina bauxite as the main refractory material, adding powder, additives, and binders, after proportioning, forming, and high-temperature sintering. High-aluminum refractory The production process of the ball is similar to that of high-alumina refractory bricks, and should be determined according to factors such as the characteristics of the raw materials and the required production conditions of the high-alumina refractory balls.
1. Strong heat storage capacity and good heat storage effect
2. Good creep properties.
3. High compressive strength and good wear resistance.
4. Good chemical stability.
5. Good high temperature resistance.
The characteristics of high alumina refractory ball
1. Strong heat storage capacity and good heat storage effect2. Good creep properties.
3. High compressive strength and good wear resistance.
4. Good chemical stability.
5. Good high temperature resistance.
The size of high alumina refractory ball
The size of high alumina refractory ball is divided into: 40mm, 50mm, 60mm, 80mm and other sizes of refractory ball. The size of high alumina ball can also be customized according to customer needs.The function of high-alumina refractory balls
The function of high-alumina refractory balls: mainly stacked in industrial kilns, which can achieve the effect of heat storage.High-aluminum refractory ball application
High-aluminum refractory ball application: It can be used in industrial furnaces such as blast furnace ironmaking hot blast furnaces, high and low temperature conversion furnaces in chemical fertilizer plants, reformers, hydroconverters, desulfurization tanks and methanation furnaces.Production process of high alumina refractory ball
1.Selection and classification of bauxite clinker
Choosing raw materials that meet the requirements is a prerequisite for the production of qualified products. High-aluminum clinker is the main raw material for the production of high-aluminum refractory balls. First of all, the bauxite clinker needs to be strictly sorted to avoid mixing. According to the quality requirements of different grades of high-alumina refractory balls, different grades of raw materials are selected, which is conducive to the rational use of raw materials, and the fine blending of fine materials to stabilize the quality.2. Fine grinding of clinker and bonded clay
Part of the bauxite clinker and the combined clay are mixed and finely ground, which is an important measure in the production of high-alumina refractory balls. It is effective in improving product quality, controlling the secondary mullite reaction in the matrix, and eliminating or weakening the influence of the secondary mullite effect on the surface of the clinker particles.3. Firing
The firing temperature of high alumina refractory balls mainly depends on the sintering characteristics of bauxite clinker. When using special grade bauxite clinker, due to the uniform and compact structure of the raw materials, the high content of impurity Fe2O3 and TiO2, the green body is easy to sinter, and the sintering temperature range is narrow, which is likely to cause over- or under-burning. Use secondary bauxite In the case of soil clinker, due to the expansion and loosening effect caused by the secondary mulliteization, the green body is not easy to sinter, so the firing temperature needs to be higher. The high alumina refractory ball can use the same firing temperature, which is 1450°C when firing in an inverted flame kiln.Relevant information
-
Silicate fire brick
Silicon thermal insulation refractory brick refers to the thermal insulation refractory products made of silica as the main raw material, with a SiO2 content of no less than 91%. In addition to the heat insulation perfor··· -
silica bricks manufacturing process
1.1 Determination of raw material ratio and particle compositionThe raw materials for making silica bricks are silica and waste bricks containing more than 96% SiO2, in addition to lime, mineralizers and organic binders.··· -
Alumina hollow ball bricks
Alumina hollow ball bricks are made of alumina hollow balls and alumina powder as the main raw materials, combined with other binders, and fired at a high temperature of 1750 degrees. It belongs to a kind of ultra-high t··· -
Anti-stripping high alumina brick for cement kiln
Anti-stripping high alumina bricks are made of high alumina bauxite clinker, mullite, kyanite, zircon sand, and binder first through granulation and powdering processes, mixed in a certain proportion, then pressed into s···