What are the products of zircon refractory bricks?
2022-03-30
The relative molecular mass of zirconia (ZrO2) is 123.2, the true density is 5.68g/cm3, the melting point is 2670°C, the Mohs hardness is 6.5 degrees, and the average linear expansion coefficient at 20~1000°C is 10×10-6/°C:, 1000 The ℃ thermal conductivity is 2.30W/(m·k). The compressive strength of zirconia ceramic products can reach 2100MPa.
Zircon products are close to acidic refractory materials and have good corrosion resistance to acidic or neutral slag. It is very stable to use under oxidizing atmosphere conditions.
At different temperatures, zirconia exists as monoclinic, tetragonal, and cubic.
What are the products of zircon refractory bricks?
Zircon bricks, pure zirconium bricks, dense zircon bricks, ordinary zircon bricks, zircon corundum bricks, zircon mullite bricks, medium zirconium bricks, zircon hollow ball bricks, etc.
Zircon refractory bricks are made by mixing, forming, drying of ingredients, and firing at high temperature in a shuttle kiln.
How about zircon refractory bricks?
Zircon brick products have dense crystal structure, high bulk density, large volume, high mechanical strength at room temperature and high temperature, good thermal shock stability, small refire shrinkage and high temperature creep, and have extremely high chemical stability and alkali resistance. Sexual medium erosion and other characteristics.
Zircon bricks, in the process of steelmaking, adopt the method of tapping and degassing, and zircon refractories have good corrosion resistance and thermal shock resistance to slag and molten steel, and are suitable for working under reduced pressure. It is widely used in the metallurgical industry as the lining of steel ladles for masonry degassing, as well as the lining of stainless steel ladles, the lining of continuous casting ladles, casting bricks, plug bricks, sleeve bricks and high temperature induction. Electric furnace lining, etc. Zircon refractory bricks have high resistance to acid slag and glass, so they are also widely used in severely damaged parts of glass kilns for smelting active glass. Zircon-based refractories also have the property of not being penetrated by metal aluminum, aluminum oxides and their slag, so they also obtain good results on the bottom of aluminum smelting.
Relevant information
-
Silicate fire brick
Silicon thermal insulation refractory brick refers to the thermal insulation refractory products made of silica as the main raw material, with a SiO2 content of no less than 91%. In addition to the heat insulation perfor··· -
silica bricks manufacturing process
1.1 Determination of raw material ratio and particle compositionThe raw materials for making silica bricks are silica and waste bricks containing more than 96% SiO2, in addition to lime, mineralizers and organic binders.··· -
Alumina hollow ball bricks
Alumina hollow ball bricks are made of alumina hollow balls and alumina powder as the main raw materials, combined with other binders, and fired at a high temperature of 1750 degrees. It belongs to a kind of ultra-high t··· -
Anti-stripping high alumina brick for cement kiln
Anti-stripping high alumina bricks are made of high alumina bauxite clinker, mullite, kyanite, zircon sand, and binder first through granulation and powdering processes, mixed in a certain proportion, then pressed into s···