Specifications of magnesium iron spinel brick
The magnesium iron spinel brick is a new product for cement kilns successfully manufactured by Henan Hongtai Kiln Refractory. It is a new generation of basic refractories with better technical content at present. Mainly used in the firing zone of large-scale new dry cement kiln: MgO-Fe2O3-Al2O3 spinel and periclase are the main crystal phases.
Features of magnesium iron spinel brick
(1) Magnesium iron spinel brick during the use process, the hot surface of the brick forms a layer of calcium iron or calcium-aluminum-iron-oxide with high viscosity, which improves the performance of the hanging kiln skin and the firmness of the kiln skin, and is suitable for protecting the lining brick. Period extension.
(2) The spinel content is high, which not only has high strength but also has excellent thermal shock resistance, and can effectively resist the chemical erosion of cement clinker liquid phase and alkali, sulfur, and other gases.
(3) Spinel and periclase have inconsistent thermal expansion during firing and cooling, and the micro-cracks formed between them can buffer the stress impact caused by temperature changes and avoid brittle bursting of lining bricks.
(4) Chromium-free and environmentally friendly.
Product model: B620/B320, B622/B322
Specifications of magnesium iron spinel brick
| Behaviors | ||
Magnesium iron spinel brick | |||
HT-MF80 | HT-MF75 | ||
Chemical %
| MgO ≥ | 84 | 80 |
Al2O3 ≤ | 2.5 | 2.5 | |
Cr2O3 ≥ | 3.6 | 3.5 | |
Fe2O3 | 6.3 | 4.4 | |
Apparent Porosity % | 17 | 17 | |
Cold Crushing Strength Mpa | 45 | 45 | |
Refractoriness under load 0.2Mpa ℃ | 1650 | 1650 | |
Bulk Density g/cm | 2.98 | 3.05 | |
Thermal Shock Resistance (1100℃ water cooling, times) | 4 | 4 |
-
Silicate fire brick
Silicon thermal insulation refractory brick refers to the thermal insulation refractory products made of silica as the main raw material, with a SiO2 content of no less than 91%. In addition to the heat insulation perfor··· -
silica bricks manufacturing process
1.1 Determination of raw material ratio and particle compositionThe raw materials for making silica bricks are silica and waste bricks containing more than 96% SiO2, in addition to lime, mineralizers and organic binders.··· -
Alumina hollow ball bricks
Alumina hollow ball bricks are made of alumina hollow balls and alumina powder as the main raw materials, combined with other binders, and fired at a high temperature of 1750 degrees. It belongs to a kind of ultra-high t··· -
Anti-stripping high alumina brick for cement kiln
Anti-stripping high alumina bricks are made of high alumina bauxite clinker, mullite, kyanite, zircon sand, and binder first through granulation and powdering processes, mixed in a certain proportion, then pressed into s···