The production process of magnesia spinel brick
1. Mixing of Magnesia spinel brick
It is carried out in a wheel rolling machine or a sand mixer, and the order of feeding is: granular material → pulp waste liquid → fine powder, and the total mixing time is not less than 10 min. Since the amount of CaO in the raw material is limited and the sintering degree of magnesia is increased, the trapping process is generally eliminated.
2. Forming of Magnesia spinel brick
Therefore, high-pressure molding can be used to make the green body density above 2.95 g/cm3. This helps to improve the performance of refractory bricks.
3. Drying of Magnesia spinel brick
During the drying process of the green body, the physical and chemical changes that occur include the evaporation of water and the hydration of magnesia.
4. Firing of Magnesia spinel brick
Therefore, the magnesia spinel brick stack should not be too high, generally around 0.8 m. Since the physical and chemical changes that occur during the calcination of materials have been basically completed during the calcination of raw materials, the main mineral composition of refractory bricks can be considered to be basically the same as that of sintered magnesite, except that the degree of reaction close to equilibrium and the uniformity of mineral composition distribution is Improved.
-
Silicate fire brick
Silicon thermal insulation refractory brick refers to the thermal insulation refractory products made of silica as the main raw material, with a SiO2 content of no less than 91%. In addition to the heat insulation perfor··· -
silica bricks manufacturing process
1.1 Determination of raw material ratio and particle compositionThe raw materials for making silica bricks are silica and waste bricks containing more than 96% SiO2, in addition to lime, mineralizers and organic binders.··· -
Alumina hollow ball bricks
Alumina hollow ball bricks are made of alumina hollow balls and alumina powder as the main raw materials, combined with other binders, and fired at a high temperature of 1750 degrees. It belongs to a kind of ultra-high t··· -
Anti-stripping high alumina brick for cement kiln
Anti-stripping high alumina bricks are made of high alumina bauxite clinker, mullite, kyanite, zircon sand, and binder first through granulation and powdering processes, mixed in a certain proportion, then pressed into s···