Silica brick introduction
Silica brick introduction
Silica brick is an acid refractory material with good resistance to acid slag erosion. The softening temperature under load is as high as 1640-1670℃, and the volume is relatively stable in long-term use at high temperature.
Silica brick main data:
Acidic refractory mainly composed of tridymite, cristobalite and a small amount of residual quartz and glass phases. The silica content is more than 94%. The true density is 2.35g/cm3. It has resistance to acid slag erosion. Higher high temperature strength. The starting temperature of softening under load is 1620-1670°C. Long-term use at high temperatures will not deform. Low thermal shock stability (1 to 4 times of heat exchange in water). Natural silica is used as raw material, and an appropriate amount of mineralizer is added to promote the transformation of quartz in the green body into tridymite. It is slowly fired at 1350-1430°C in a reducing atmosphere. When heated to 1450 ℃, the total volume expansion is about 1.5~2.2%. This residual expansion will make the slits close and ensure the masonry has good air tightness and structural strength.
What’s important for silica brick
The properties and process of silica bricks are closely related to the crystal transformation of SiO2. Therefore, the true specific gravity is an important quality indicator of silica bricks. The general requirement is below 2.38, and the high-quality silica brick should be below 2.35. The true specific gravity is small, which reflects that the amount of tridymite and cristobalite in the brick is large, and the amount of residual quartz is small, so the residual linear expansion is small, and the strength drop in use is also small.
-
Silicate fire brick
Silicon thermal insulation refractory brick refers to the thermal insulation refractory products made of silica as the main raw material, with a SiO2 content of no less than 91%. In addition to the heat insulation perfor··· -
silica bricks manufacturing process
1.1 Determination of raw material ratio and particle compositionThe raw materials for making silica bricks are silica and waste bricks containing more than 96% SiO2, in addition to lime, mineralizers and organic binders.··· -
Alumina hollow ball bricks
Alumina hollow ball bricks are made of alumina hollow balls and alumina powder as the main raw materials, combined with other binders, and fired at a high temperature of 1750 degrees. It belongs to a kind of ultra-high t··· -
Anti-stripping high alumina brick for cement kiln
Anti-stripping high alumina bricks are made of high alumina bauxite clinker, mullite, kyanite, zircon sand, and binder first through granulation and powdering processes, mixed in a certain proportion, then pressed into s···