Construction and Application of High Alumina Castable Refractory
With the continuous increase of blast furnace hot air temperature, higher requirements are put forward for high-alumina castables' high-temperature creep performance, thermal shock stability performance, load softening temperature, etc. According to the investigation, a high-strength, non-shrinking high-alumina castable was developed on the basis of the original high-alumina castable, and its formula was adjusted as follows:
(1) The use temperature of the castable is above 1400 °C, and a certain raw material must be added to offset the high temperature shrinkage performance of the product through a high temperature reaction.
(2) Adding metal silicon powder during high temperature use of castables can completely solve the drawbacks of high temperature shrinkage, offset its high temperature creep, and reduce shrinkage cracks during high temperature use. Its addition effect is better than kyanite and andalusite.
(3) The addition of silicon metal in the castable is 1%, and the product can have better high temperature performance, especially shrinkage resistance.
Construction and Application
1. Pouring construction
Put the material into the double-shaft forced mixer, dry mix for 1~2min, control the water amount of 5%~5.5%, add 90% of the water amount first, and adjust the water amount according to the season and construction environment, but the water amount should not be added. Beyond the control range, increased moisture will reduce strength and performance. Pour the material into the mold, and vibrate it with a vibrating rod while feeding. It requires vibrating. Each batch of 500kg is completed within 6 minutes. The interval between batches should not exceed 6 minutes, and the interval should be shortened as much as possible to prevent product delamination.
2. Demoulding and baking
The demoulding time can be 24 hours in spring and autumn, and 8 hours in summer. In winter, it should be formed in sunny days (larger construction bodies are generally formed outdoors). It is suitable to extend the demoulding time to about 1 day, to prevent the products from being frozen . Prevent the generation of surface mesh cracks. The baking temperature is above 200℃.
3. Use effect
High-strength, non-shrinking and high-alumina castables are used in blast furnaces, rotary kilns, heating furnace tops, sintering machine igniters and other parts.
-
Silicate fire brick
Silicon thermal insulation refractory brick refers to the thermal insulation refractory products made of silica as the main raw material, with a SiO2 content of no less than 91%. In addition to the heat insulation perfor··· -
silica bricks manufacturing process
1.1 Determination of raw material ratio and particle compositionThe raw materials for making silica bricks are silica and waste bricks containing more than 96% SiO2, in addition to lime, mineralizers and organic binders.··· -
Alumina hollow ball bricks
Alumina hollow ball bricks are made of alumina hollow balls and alumina powder as the main raw materials, combined with other binders, and fired at a high temperature of 1750 degrees. It belongs to a kind of ultra-high t··· -
Anti-stripping high alumina brick for cement kiln
Anti-stripping high alumina bricks are made of high alumina bauxite clinker, mullite, kyanite, zircon sand, and binder first through granulation and powdering processes, mixed in a certain proportion, then pressed into s···