Raw material of carbon brick for blast furnace 
carbon brick for blast furnace raw materials include anthracite, coke and graphite, as well as binders such as asphalt, tar and anthracene oil. Anthracite has less volatile content and a dense structure. When producing carbon bricks, it is mostly used as aggregate, metallurgical coke (coal coke) is added, and asphalt is used as a binder.

Production Process of carbon brick for blast furnace 
The production process of carbon bricks is roughly similar to other refractory bricks, but it must prevent the oxidation of carbon at high temperatures, so the baking of raw materials and the firing of products must be carried out in a reducing atmosphere.
The carbon brick for blast furnace ingredients are roasted granular anthracite as aggregate, the firing temperature is 1300~1450℃, the holding time is about 20 hours, the total firing time is about 240~420 hours, and the kiln is cooled to 40~60℃. Carbon bricks leave the kiln at high temperature, which is easy to catch fire.

Feature of the carbon brick for blast furnace 
carbon brick for blast furnace has good thermal stability, small thermal expansion coefficient, high temperature resistance, resistance to various acids, alkalis, salts and organic solvents, but it is easily oxidized in an oxidizing atmosphere.

Use of the carbon brick for blast furnace 
Carbon bricks are widely used in the metallurgical industry. Among them, the blast furnace carbon brick for blast furnace is the most used, and the bottom and hearth of many blast furnaces are made of carbon brick for blast furnace . Carbon bricks are also used in aluminum electrolytic cells. In addition, it is also widely used in pickling tanks, electroplating tanks in the electroplating industry, dissolution tanks in the paper industry, reaction tanks and storage tanks in the chemical industry, and autoclaves in the petrochemical industry.