The high melting temperature of the glass melting furnace, the sensitivity of the kiln body size to temperature changes and the thermal expansion of the kiln refractory materials all require that special attention should be paid to the temperature rise of the glass me··· ...

(1)BurnerEach part of the Burner includes the flat wall of the Burner crater, the Burner stack, the burner brick, the burner brick stack, the burner slope wall, the vertical wall, the burner side wall, the burner bottom and the burner inlet wall connected to the regen··· ...

Silica bricks for glass kilns refer to silica refractory products used in high-temperature parts of glass kilns (not in contact with glass liquid). Glass kilns are complex and large masonry built of various refractory materials, and their vaults are mostly made of sil··· ...

Electro-fused aluminium-zirconium-silica (AZS) bricks are mostly used in high-temperature parts of the kiln and in parts severely corroded by glass liquid. Different brick models are usually marked by the amount of ZrO2. The brick is mainly composed of two crystal pha··· ...

High chrome bricks are made of industrial grade chromium trioxide and alumina as the main raw materials, or a small amount of zirconia, etc., and fired at high temperature to obtain a shaped refractory product with a chromium trioxide content of not less than 75%, and··· ...

As a common brick for glass melting furnace, mullite brick can be used in many parts of glass furnace. The following is the application of mullite brick in various parts of glass melting furnace.1. Front wallThe front wall of the glass melting furnace is close to the ··· ...

The application of high chrome bricks in glass kilns is mainly due to their excellent corrosion resistance and high temperature resistance. The following are some key points of the application of high chrome bricks in glass kilns:Strong corrosion resistance: High chro··· ...

In the glass manufacturing industry, the same glass products and the same glass kilns have different maintenance times, maintenance locations, and kiln service lives. Normal material erosion is erosion within the design service life of the material, while abnormal mat··· ...

The bubbles caused by the contact between impurities or pores in the refractory material and glass liquid are called refractory bubbles.Factors such as the porosity, iron content, and carbon content of refractory materials will cause the formation of bubbles through c··· ...

When refractory materials are used in glass kilns, they will be severely damaged due to high temperature, flame, powder, atmosphere, air flow and liquid flow, which greatly affects the service life of the kiln. The use of refractory materials in kilns begins from the ··· ...